Fire Clay Bricks

Home › Products Bricks › Fire Clay Bricks

We specialize in fabricating Refractory Fire Bricks from quality clay. Our Fire Clay Bricks are developed with various proportions of B.D., C.C.S, P.C.E, R.U.L and P.L.C. Our collection of Refractory Fire Bricks is globally accepted for high compression ratio, high tensile strength and good uniformity. Our Refractory Fire Bricks can withstand high heat and temperature. We are well reckoned as one of the flourishing Ceramic Fire Bricks Manufacturers and Suppliers based in India. We provide Refractory Fire Bricks within the stipulated time frame at very affordable prices.

Specifications

High Alumina Refractory Bricks
IS : 6 & IS : 8
High Alumina Refractory Tiles & Blocks
Shape Bricks

Refractory Fire Bricks

Note
- Provided above are average test data, subject to reasonable variations
- The above specifications relate to machine-pressed standard bricks only
- The AP, BD and CCS values are arithmetic mean of five individual results
- Low ferric bricks also available
- Size tolerance: Variation from specified dimensions, covering both warpage and shrinkage shall be allowed to the extent of ±2% or ±2 mm, whichever is greater

Generally Used In

Cast iron foundries
Cupolas
Rolling Mills
Lancashire Boilers
Rice Mill
Mini Steel PlantsvBoiler Arches
High Pressure Boilers
Checkers of open hearth furnaces
Oil fired furnaces
Glass Factories

Technical Specification

DRY PRESSED BRICKS	JMD IS-7	JMD IS-6	JMD-CFCT	JMD IS-8	JMD-45	JMD-50	JMD-40D
Chemical Properties
Al2O3-% min.	24	30	35	40	45	50	40
Fe2O3-% max.	2.00	2.00	2.25	2.50	3.00	3.00	2.00
Physical Properties
A.P-% max	27	25	24	24	23	23	21
B.D- (gm/cc)-min	1.90	2.00	2.10	2.10	2.20	2.30	2.20
C.C.S.(Kg/Cm2) min	250	250	300	350	380	400	350
Thermal Properties
P.C.E(O.C) min	29	30	31	32	32.5	33	32.5
R.U.L (Ta oC at 2kg/cm2) min	1290	1300	1330	1400	1400	1400	1420
P.L.C % max/2 hrs.	.+/- 1.00 at 1300 oC/2hrs	.+/- 1.00 at 1300 oC/2hrs	.+/- 1.00 at 1350 oC/2hrs	.+/- 1.00 at 1400 oC/2hrs	.+/- 1.00 at 1400 oC/2hrs	.+/- 1.00 at 1450 oC/2hrs	.+/- 1.00 at 1450 oC/2hrs
Application Area	Chimeny flue, Boiler & Sugar industry	Chimeny flue, Boiler & Sugar industry	Chimeny flue, Boiler, Cupola & Steel industry	Cement preheater, cyclone, boiler incinerators, silicate furnace	Cement preheater, cyclone, boiler incinerators, silicate furnace	Cement kiln,preheating zone, preheating furnace wall	Cement preheater,cyclone incinerators,silicate furnace

Note

The above dataare on average result basis of pressed standard bricks & may vary on actual.
Size Tolerance : +/-1.5% OR +/- 2.0mm whichever is higher.

Note:

Provided above are average test data, subject to reasonable variations
The above specifications relate to machine-pressed standard bricks only
The AP, BD and CCS values are arithmetic mean of five individual results
Low ferric bricks also available
Size tolerance: Variation from specified dimensions, covering both warpage and shrinkage shall be allowed to the extent of ±2% or ±2 mm, whichever is greater

* fields are mandatory

ENQUIRY FORM

Contact Information
Contact Person *
Company Name *
Address *
Country *
Email ID *
Phone Number
Mobile Number *
Fax
Details
Subject *
Details *
Verification Code *