| Acid Resistant Castable |
| Properties |
Typical Properties |
Spesification |
| 700 |
700 |
| Max. Service Temperature (deg. C) |
| Bulk Desity (kg/m3) |
| After Drying at 110 deg. C |
2055 |
2050 (min) |
| Thermal Conductivity (W/mk) |
| At 300deg. C H.F. |
0.65 |
0.7 (max) |
| At 500 deg. C H.F |
0.67 |
0.7 (max) |
| C.C.S. (kg/cm2) |
| After Drying at 110 deg. C |
225 |
210 (min) |
| After Drying at 400 deg. C |
264 |
250(min) |
| After Drying at 800 deg. C |
325 |
320 (min) |
| M.O.R (kg/cm2) |
| After Drying at 110 deg. C |
65 |
60(min) |
| After Drying at 500 deg. C |
28 |
25 (min) |
| Linear Shrinkage (%) |
| After Drying at 110 deg. C |
-0.08 |
,-0.1(max) |
| After Drying at 500 deg. C |
-0.17 |
,-0.2(max) |
| Chemical Compositor |
| Al2o3 (%) |
15 - 20 |
15 -20 |
| SiO2 (%) |
70 -75 |
70 - 75 |
| Shelf Life ( months) |
12 |
- |